As mentioned before, pressureless sintering of specimens containing additions of Y2O3 and SiO2 essentially show no densification at all because of the evaporation of SiO2 at the sintering temperature. In contrast, the use of hipping, applying a pressure of 100 MPa, allowed full density to be achieved in these specimens. In this case, the solidification of the liquid phase formed at the hipping temperature led to the formation of crystalline intergranular phases at all temperatures: however, the chemical compositions of the intergranular phases formed in the specimens with and without carbon additions were different, since for high carbon contents the resulting intergranular phase was observed to be richer in Yttrium(85% at Y/15% at Si).
On the other hand, it must be emphasised that the crystallinity of the intergranular phases obtained in these specimens was disrupted as Al2O3 was added as a third addition to the powder mixture. For these specimens in all cases
3.2.2 HIP
如之前提到的，添加了Y2O3和SiO2的样本的无压烧结基本上不会出现稠化现象，而原因正是由于烧结温度下SiO2的蒸发。与此相比，采用加压，例如添加100MPa，则会使产物达到完全的高密。在这种情况下，加压温度下液态产物的凝固在所有温度范围下都将生成间粒晶体：但是，是否添加了碳则将会使产物晶体的化学成分发生不同，因为在高碳含量下，产物晶体会更富含钇(85%Y比15%Si)
另一方面，我们必须强调的时，如果Al2O3作为第三方物质加入反应混合物粉末中，那么产物晶体的结晶度将被破坏。对于这之下的所有情况，产物都将会近似玻璃质晶体，而这一点已被广泛证明。化学成分，根据EDS的以半定量方式验定为如下，13.8%Y, 15.7%Si, 7.5%Al, 63.1% O.我们也应提到，SiC加Y2O3和Al2O3的混合物(不含SiO2)与实验温度范围内的无压烧结时一样，所生成的YAG也是晶体态的。此外，除非反应物原始SiC粉末中包含了α，否则，在任何加压情况下，都不会这个转化。
3.2.2. HIP
如上所述，包含Y2O3的加法的pressureless焊接标本和SiO2本质上不显示浓缩由于SiO2的蒸发在焊接温度。 相反，使用hipping，施加100 MPa压力，提供充分的密度达到在这些标本。 在这种情况下，固体化液体阶段被形成在hipping的温度导致了水晶晶粒间的阶段的形成在所有温度： 然而，在标本形成的晶粒间的阶段的化学成分有和没有碳加法是不同的，因为为高碳内容发生的晶粒间的阶段被观察是富有在钇(85%上在Y/15%在Si)。 在另一只手，必须强调打乱了在这些标本得到的晶粒间的阶段的结晶性，当Al2O3增加了作为第三加法到粉末混合物。 对于这些标本一个玻璃状晶粒间的阶段由不同的作者在所有的情况下观察，一样坚定，并且它的构成，取决于以半定量方式EDS，也许被写象13.8at% Y， 15.7at% Si， 7.5at% Al， 63.1at% O。 也许在PS之前也提及SiC+Y2O3–Al2O3构成(没有SiO2)导致与YAG的标本作为晶粒间的阶段，同一样，形成在所有
experimental使用的温度范围。 此外，除非原始的SiC粉末包含的一些种子，变革没有在任何h