DEEP DRAWING

来源：百度知道 编辑：UC知道 时间：2024/06/06 04:43:15
Where D = blank diameter
d = punch diameter
The calculation is usually made with the cup-wall inside diameter , which would also be the draw-punch diameter . A drawing ratio or percentage reduction of 48％ is considered excellent on the first draw . Succeeding draws must be reduced . That is the percentage reduction that can be expected under favorable conditions without annealing , for a second draw would be about 30％ and about 20％ for a third draw.
Most drawing operations start with a sheet metal blank whose surface area is only slightly larger than the finished product , allowing just enough material to hold the blank during the drawing operations and for trimming after drawing.
There should be no appreciable change in the thickness of the material between the blank and the finished part . When it is desirable to reduce the metal thickness , it may be done in secondary operations as in ironing .
The die cushion , which is underneath the press bed , holds t

其中D =空白直径
d =凸模直径
计算通常是用杯子壁内直径，这也将成为吸引冲孔直径。绘图比率或百分比减少了48 ％认为是极好的第一抽奖。传承提请必须减少。这是削减百分比，可以预期的有利条件下的退火，第二次提请将约30 ％和20 ％左右的三分之一抽奖。
大多数绘图行动开始，金属薄板的空白，其面积只略大于成品，使刚刚足够的材料的空白举行期间，利用业务和后提请微调。
应该没有明显的变化，厚度的材料之间的空白，并完成部分。当它是可取的，以减少金属的厚度，可以进行二次行动中熨烫。
模具垫，这是下面的新闻床，持有的空白对冲压在initail阶段的运作。然后，作为冲压下降，缓冲也将下降，保持联系的空白。当中风完成，模具缓冲返回其原来的立场，冲水与上方的冲压。这一行动的一部分带了吧。出版社不是通常配有死的缓冲时间，但此附件大大扩展了多功能的新闻。缓冲可能是春季，空气，或液压驱动。
由于金属开始走向死亡，发生弯曲。 Creater深度obtainde利用或金属拉从法兰地区。底部的杯子是完成了第一阶段。非常大，发生部队压缩在法兰和死亡半径领域。通常情况下，皱纹开始形成的金属退出的死亡半径。幸运的是，正确运用空白持有人可以随时从皱纹的金属退出的死亡半径。幸运的是，正确运用空白持有人可以随时皱纹的形成。但是，如果空白控股的压力太大，金属撕裂。
最后一个阶段是一个延续前两个阶段的弯曲，压缩，克服摩擦，和拉直。
重要变数的绘图操作摩擦， squesszing力量，成形的金属。
数额遇到的摩擦将取决于表面的金属部件和模具的空白，并持生效。摩擦通常是减少使用适当的绘图化合物。
挤压的力量，发生在法兰盘半径，并提请有关的百分比reductionof地区，延性屈服强度，空白的厚度，温度和深度的利用，如何以及金属形式将governde的应变硬化指数和平均应变率。