EXPERIMENTS ON STEEL PLATES
Before the process is tested on aluminum, 12.7mm (0.5 inch) thick DH-36 plates have been used to examine if a stable Dual Bypass GMAW can be achieved. To this end, the following parameters have been used:
• Left bypass shielding gas (100% Argon): 10.4 liter/min (22 CFH)
• Right bypass shielding gas (100% Argon): 10.4 liter/min (22 CFH)
• GMAW torch shielding gas (100% Argon): 9.4liter/min (20 CFH)
• Diameters of tungsten electrodes: 2.4 mm
• Wire Feed Speed: 12.6 m/min (496 IPM)
• Diameter of the steel wire: 1.2 mm
• Travel speed: 12 mm/s (28 IPM)
• CV power supply voltage setting: 32 Volts
It was found that a stable Dual Bypass GMAW process can be achieved with the following torch installation parameters: d1 = 4mm, d2 = 3mm, d3 = 17mm, d4 = 9mm. Fig. 4 shows the resultant weld bead made using the following
实验钢板
在测试的过程是对铝，一十二点七毫米（ 0.5英寸）厚鮬- 36板已被用来研究是否稳定双旁路气体保护焊是可以实现的。为此，下列参数已被用于：
•左旁路保护气体（氩气100 ％ ） ： 10.4升/分钟（ 22 CFH ）
•权旁路保护气体（氩气100 ％ ） ： 10.4升/分钟（ 22 CFH ）
•气体保护焊炬保护气体（氩气100 ％ ） ： 9.4liter/min （ 20 CFH ）
•直径的钨电极：二点四毫米
•送丝速度： 12.6米/分（ 496的IPM ）
•直径钢丝： 1.2毫米
•行走速度： 12毫米/秒（ 28的IPM ）
•简历设置电源电压： 32伏特
结果发现，一个稳定的双绕道气体保护焊的过程，才能实现以下火炬安装参数：素D1 =四毫米， D2类= 3毫米，维生素D3 = 17毫米， D4类= 9毫米。图。 4显示了由此产生的焊缝珠使用下列参数：
•左旁路电流：约80 -百安培
•右旁路电流：约70 - 90安培
•贱金属电流：约70 - 80安培
图片显示，当所有弧存在，熔融金属不能扩散到广泛的基本金属，因为基本金属热输入相对较低。结束时的焊珠（左年底的图片） ，焊缝珠传播更多断然。人们怀疑，减少沉积和同热输入负责。
在钢板器皿上试验 在过程存在测验右手击球员的左后方场地铝之前,如果一稳定双的旁路的GMAW能被取得,12.7mm(0.5英寸)厚DH-36器皿已经被用来进行检查.为此,下列的参数已经被使用: •往左绕过保护气体((100%氩):10.4升//分钟((22 CFH)•正确绕过保护气体((100%氩):10.4升//分钟((22 CFH)•保护气体((100%氩)GMAW火炬:9.4liter/min(20 CFH)•钨电极的直径:2.4毫米•电报喂速度:12.6米 /分钟((496 IPM