2. MEA fabrication and single-cell performance measurements
The catalysts tested in the present study were applied as anode
catalysts and a commercial Pt black catalyst (Johnson Matthey)
was applied as the cathode catalyst. The catalyst-coatedmembrane
(CCM) was constructed by spraying the catalyst ink directly on to
the polymer electrolyte membrane. Nafion 115 was used as the
membrane, and the catalyst loadingwas 1.5mg cm−2 on both sides
of the membrane. Anode and cathode gas-diffusion layers were
then placed on both sides of the CCM [13]. Polarization curves for
each MEA were measured in individual 5 cm2 cells. The MEA was
placed between two gas-diffusion layers (GDLs), inserted into two
graphite plates that contained a serpentine flow-field, and then
assembled at
你这又长又专业，追加点赏分吧。
1. 论文题目 Modified polyol synthesis of PtRu/C for high metal loading and effect of post-treatment
用于高金属沉积和后处理效应的PtRu/C的改进多元醇合成
我选了一段 帮我下。。
2. MEA fabrication and single-cell performance measurements
MEA（薄膜电极接合体？）的制造和单（电）池性能的测量
The catalysts tested in the present study were applied as anode
catalysts and a commercial Pt black catalyst (Johnson Matthey)
was applied as the cathode catalyst. 本研究中试验的催化剂被用作阳极催化剂，而一种商品级的铂黑催化剂（Johnson Matthey公司出品）被用作阴极催化剂。PtThe catalyst-coated membrane(CCM) was constructed by spraying the catalyst ink directly on to
the polymer electrolyte membrane. 由催化剂涂覆的隔膜（CCM）通过将催化剂油墨直接喷涂到聚合物电解质隔膜上而构成。Nafion 115 was used as the
membrane, and the catalyst loadingwas 1.5mg cm−2 on both sides
of the membrane. Nafion115被用作隔膜，催化剂的沉积为隔膜两面各1.5mg cm−2。
Anode and cathode gas-diffusion layers were
then placed on both sides of the CCM [13]. 然后阳极和阴极气体扩散层被置于CCM的两面。Polari