The synthesis of binary metal sulfides has been the focus of attention because of their important physical and chemical properties [1, 2], good commercial applications in semiconductors, pigments, luminescence devices, solar cells, IR detectors and optical fiber, communications, modern thermoelectric coolers [3]. Bismuth sulfide (Bi2S3) is a direct band gap material with Eg of 1.3 eV [4] and useful for photodiode arrays of photovoltaics [5]. Usually, busmuth sulfide can be prepared by direct reaction of bismuth and sulfur vapor in a quartz vessel at high temperature [6]. The chemical deposition method was applied to prepare bismuth sulfide through reaction of bismuth salt complexed by triethanolamine or EDTA with an aqueous solution containing a sulfur sourse such as thioacetamide, thiourea, sodium thiosulphate, geseous H2S. However, the powders obtained through this route are mostly amorphous or poorly crystallized [7–1
超细粉体的合成二元硫铋金属硫化物一直关注的焦点,由于其重要的物理和化学性质[12〕、良好的商务应用半导体、颜料、发光器件、太阳能电池、红外探测器、光纤、通讯、现代热电冷却器[3].铋硫化物(备Bi2S3)是直接带隙的材料如130电动[4]和有益的光电二极管列阵[5].通常busmuth硫化物可以直接反应制备了铋、硫磺蒸气船石英高温[6].化学沉积方法用于准备硫化铋铋盐络合的反应,通过乙醇胺水溶液或edta一个含有硫源为硫代乙酰胺等,硫、硫代硫酸钠、硫化氢geseous.但是,这条线路大多透过粉末定形或结晶差〔7月10日].热分解制备铋硫化物还报告了热分解物[11]荒铋、金属ethylxanthate[12],双硫复杂[13].然而,所有这些方法需要高温或含有某些impurites最后翻版.一些研究使用nonagueous解沉积铋硫化物薄膜,但他们的产品有定形[14,15].渝黔报备Bi2S3通过热合成反应及硫乙醇bicl3140℃[16].
因为全文我看过知道那些数字指的是参考资料就没加进去
超微（非常小的颗粒）硫化铋准备
二元金属铋的合成，由于它的重要的物理和化学特性而成为人们关注的焦点。
在半导体，颜料，冷光设备，太阳能电池，信息检索器和光纤，通讯，热电冷却器等方面都有着出色的商业应用。硫化铋(Bi2S3)是一种直接能隙材料，eg值为1.3ev.对光电池中的光电二极管排列很有用。通常情况下硫化铋可以直接由铋和硫蒸气在水晶容器中高温下反应合成。化学沉淀法可以用来准备硫化铋通过三乙醇胺和铋盐的反应或者由乙二胺四乙酸和含硫代物水溶液（如硫代乙酰胺，硫脲，硫代硫酸钠，硫化氢气体）反应。然而通过这中方法得到的粉末通常是非结晶质的或者结晶不良好的。硫化铋的热分解准备同样在硫代氨基甲酸铋复合物、乙基磺原酸镍、双硫脲复合物的热分解中有提到过。然而，上述的这些方法需要在高温中进行，否则最终的产物将会含有一些杂质。有些研究用非水溶液沉淀硫化铋薄膜，但他们得到的是非结晶质的产物。Yu和Qian的报告中说硫化铋的合成是通过BiCl3和硫脲酒精溶液在140°C下反应。
超细粉体的合成二元硫铋金属硫化物一直关注的焦点,由于其重要的物理和化学性质[12〕、良好的商务应用半导体、颜料、发光器件、太阳能电池、红外探测器、光纤