After pre-processing to exclude spurious objects,
the Minkowski–Bouligand method, which is used to
compute fractal dimension of profiles, was applied by
means of a macro program based on morphological
operations of dilatation and erosion according to Fig.
1c and d [15]. This macro program reproduces the
sequence proposed by Russ [10], where a sequence of
dilations and erosions from a binary representation of
eroded profile produces a sausage, as described on
Fig. 1e.

In order to analyse the microstructural variation of
material along of profile, a qualitative analysis was
done. Polished region profile was etched by immersion in an aqueous solution with 2 wt.% HF. Etching
reveals the microstructure and is sensitive to polarised
light. Fig. 2 is a montage showing microstructural
evolution along eroded profile.

This orientation of lamellae can be related to
eroded surface reli

预处理后排除假货的物体,minkowski-bouligand法,这是用来计算分数维概况 是采用了一种宏观规划基于形态学的业务扩张和侵蚀据无花果. 1c和d〔15〕. 这一宏观programreproduces顺序提出russ〔10〕, 凡序列dilationsanderosions从二进制表示侵蚀剖面产生香肠 形容对无花果. 1e. 为了分析微观物质沿剖面,定性分析. 珠圆玉润地区廓布满沉浸在水溶液中以288.1%. 成巨星. 蚀刻揭示微观结构和敏感polarisedlight. 无花果. 二是表现蒙太奇microstructuralevolution沿侵蚀剖面. 这个方向lamellae可与地表侵蚀救济. hebesberger〔16〕建立了关系,微观导向和断口. 工人没有找到一个定量关系,这两个参数, 但他们已确定裂缝路径方向晶体晶粒的金属材料. 因此可以合理地假设这随机性对微观方向也可以表达不同的地方形 维值沿剖面的侵蚀. 定性关系crystallographicorientation这个标本和结构形维已发现在这方面的工作, 如图. 3a. 更大的价值和较大的分散可以看出,在四大地区分析积(第一和第二 宿舍遭侵蚀的姿态从一开始). 无花果. 3b展品最高价值的差额骤积地区. 这些结果就观察显微自更异质的微观约浆现象有关 质地形维 也有人认为,最高的价值观念的差异,在形的阴谋,是在第一季度的弹坑, 而其他地区保持同样的价值观(图3d). 这可以合理适当的改变消退动能整个表面弹坑. 颗粒通量罢工标本的攻角30j以及这些颗粒旅行标本 他们增加了倾斜角度. 因此,这种现象是有更多的精力在第一试区,相当于正常组成浆料 变形成了较大的增加,对倾斜角[17,18]. 这意味着表面粗糙度在开始区域和更顺利地在结尾之一, 这是协议构造分维值在这项工作中,如图. 116和D.