Polishing:
To polish use XPAL, Alox 721 or comparable material. Polishing should require a maximum of 20 seconds under the above machining conditions.
Hydration:
Lens made with G-Materials will hydrate much faster than lenses made from other materials of comparable water content. Place lenses into the Borate Buffer pH 7.2 isotonic saline and allow the lens to sit in solution while stirring for a minimum of 6 hours. Hydrate for the minimum time specified at constant temperature (T = 20± 2°C). A minimum of 10 ml per lens should be used for hydration.
After hydration, lenses should be rinsed, autoclaved, and store in the pH 7.2 buffered saline solution for packaging and sterilization.
Isotonic Saline:
Borate Buffer
pH 7.2; 295 mOs
NaCl 8.01 grams
H3BO3 2.47 grams
Na2B4O7 . 10H2O 0.14 grams
The weights for the buffered saline formulas are based on a 1 Liter Volume solution. The borate solution s
To polish use XPAL, Alox 721 or comparable material. Polishing should require a maximum of 20 seconds under the above machining conditions.
Hydration:
Lens made with G-Materials will hydrate much faster than lenses made from other materials of comparable water content. Place lenses into the Borate Buffer pH 7.2 isotonic saline and allow the lens to sit in solution while stirring for a minimum of 6 hours. Hydrate for the minimum time specified at constant temperature (T = 20± 2°C). A minimum of 10 ml per lens should be used for hydration.
After hydration, lenses should be rinsed, autoclaved, and store in the pH 7.2 buffered saline solution for packaging and sterilization.
Isotonic Saline:
Borate Buffer
pH 7.2; 295 mOs
NaCl 8.01 grams
H3BO3 2.47 grams
Na2B4O7 . 10H2O 0.14 grams
The weights for the buffered saline formulas are based on a 1 Liter Volume solution. The borate solution s
擦亮用途XPAL、Alox 721或可比较的材料。 波兰语应该在上面用机器制造的条件下需要最多20秒。
Hydration ： 用G材料做的Lens比由可比较的水含量其他材料做的透镜快速地将水合。 安置透镜入硼酸盐缓冲酸碱度7.2等渗盐并且允许透镜坐在解答，当搅动在至少6个小时时。 极小的时间的含水物指定在恒温(T = 20± 2°C)。 应该为水合作用使用至少10 ml每个透镜。
应该漂洗After水合作用，透镜，真空加热，并且酸碱度的7.2商店缓冲了包装和绝育的食盐水。
盐的Isotonic ：
Borate缓冲
pH 7.2; 295 mOs
NaCl 8.01克
H3BO3 2.47克
Na2B4O7. 10H2O 0.14克
缓冲的盐惯例的The重量根据一种1公升容量解答。 硼酸盐解答通过绝育过程(真空加热)和叶子显示优秀表现免于透镜残滓。