A number of routes for hydrogen production for various applications have been proposed and the most promising one appears to be the use of methanol as a chemical carrier, mainly due to the advantages of methanol storage and transportation. In steam reforming of methanol, copper catalysts exhibit high selectivity [35–37]. Over group VIII metal catalysts, CO is predominantly produced along with CO2 and H2. The selectivity for the steam reforming over group VIII metal catalysts is much lower than that for copper catalysts [38].
Catalytic steam reforming of methanol over skeletal Cu catalysts has been carried out. An earlier study [28], in which Cr2O3 was added to skeletal copper by leaching CuAl2 alloy particles in aqueous NaOH solutions containing sodium chromate, showed that the addition of Cr2O3 enhances the copper surface area significantly by improving the structure of skeletal copper and the
手工翻译
3.4. 添加剂在甲醇蒸汽重组反应中的作用
对于不同应用的氢制造方法有很多，其中一个最有前途的方法是采用甲醇作为化学载体，这主要归因于甲醇存储和运输极为便利。在甲醇的蒸汽重组中，铜催化有很强的选择性 [35-37]。在VIII组金属催化中，一氧化碳的产生量远远大于二氧化碳和氢气VIII组蒸汽重组的选择性比铜催化的选择性低很多 [38].
在铜骨骼上的甲醇催化重整的研究已经进行。在早期的研究中[28]，通过过滤含有钠硝酸盐的水性氢氧化钠中的二铝化铜颗粒，将三氧化二铜加到骨骼铜上，试验表明三氧化二铜添加剂改进了骨骼铜的结构，改善了MSR的活跃性，从而大大增强了铜表面区域。结果表明，在该反应中，铜骨骼中的最佳三氧化二铜含量是 0.5wt%.
这一项研究中测量了甲醇蒸汽重组反应中的活跃性和选择性，并在图5和图6中分别列出了数据。从图5中，我们可以看到表面上少量的三氧化二铜可以大大提高活跃性。进一步的增加三氧化二铜将会导致铜表面的减少（图1）和降低MSR反应的活跃性（图5）。总体来说，提升的催化要优于未提升的催化。进一步的，少量三氧化二铜的添加将会降低一氧化碳的产生，如图6所示。
显然，铜表面上的少量的三氧化二铜(0.2 wt%)将会提高甲醇蒸汽重组中的骨骼铜的活跃性和选择性。尽管使用了截然不同的向骨骼铜催化剂中添加三氧化二铜的方法，该研究结果与早期发现[28]一致。
氧化锌添加剂的存在也会对甲醇蒸汽重组的活跃性和选择性起到积极作用。钴添加剂也可以提高活跃性，但它会产生将甲醇分解成一氧化碳的不良结果（公式9）。
3.4. 在甲醇上的添加剂的效果蒸发改革
反应
若干的路径为氢制造对于各种不同的申请已经被计划，而且一个最有希望的似乎是如一个化学的运送者的甲醇使用, 主要适当对甲醇储藏和运输的利益。 在蒸气方面甲醇的改革,铜催化剂展现高的选择性 [35 – 37] 。 在团体之上 8个金属催化剂,CO 居多被连同 CO2 和 H2 一起生产。 为在团体之上改革 8个金属催化剂的蒸气选择性比铜催化剂低许多 [38].
接触反应的蒸气在骨骼的 Cu 催化剂上的甲醇改革已经被实行。一项较