In conclusion, we demonstrated, both theoretically and experimentally, that C-doped ZnO is ferromagnetic at room temperature. Carbon-doped ZnO films show an intrinsic n-typed ferromagnetic behavior, with Curie temperatures well above room temperature. The intrinsic ferromagnetism originates from the Zn-C system in the ZnO environment. Our work demonstrates that carbon is a novel dopant in the class of doped ZnO dilute magnetic semiconductor materials.
Y. P. Feng wishes to thank Zhenyu Zhang for useful discussion on the topic, and acknowledges financial support from the National University of Singapore Academic Research Fund under Grant No. R-144-000-182-112.
Y. P. Feng wishes to thank Zhenyu Zhang for useful discussion on the topic, and acknowledges financial support from the National University of Singapore Academic Research Fund under Grant No. R-144-000-182-112.
结论，我们在理论和实验都证明，碳浸渍氧化锌在室温下是磁体。碳浸渍氧化锌薄片在高于室温的居里温度下表现出固有的N型磁体行为。这种固有的磁性来自于氧化锌环境中的锌-碳系统。我们的工作证明了碳是一种新的属于氧化锌掺杂务半导体材料。
FENG.Y.P非常感谢张振宇，谢谢在此课题中非常有帮助的讨论。同时也感谢新加坡国立大学学术研究基金课题NO R-144-000-182-112. 给予的资金方面的支持。
部分词语翻译不当，你在研究研究！
总之,我们证明,从理论和实验两方面,C-doped氧化锌是铁磁室温。Carbon-doped氧化锌films显示出内在n-typed居里温度、铁磁行为远远高于室温。内在的铁磁性源于Zn-C制度环境。氧化锌我们的工作表明碳是一种新型的柘在磁性半导体材料掺杂纳米氧化锌稀释。
冯y .谢谢兄弟张的愿望的讨论话题,有用的支持,也承认financial新加坡国立大学的学术研究基金的资助下。R-144 - 000 - 182 - 112。