The plastic joints under study are made through an extrusion molding process. The material involved is a composite of two layers of a polymer (High Density Polyethylene HDPE) with an adhesive interface. This composition is shown in Fig. 1. Carbon pigments have been added to one of HDPE layers for darkening to provide better thermal absorption and emission properties for insulation purposes. The geometry of the joints under inspection along with a cross section are shown in Fig. 2, this geometry is represented in two cups welded together at the neck region. The bond interface is located between the white HDPE layer and the rest of the geometry.

Display Full Size version of this image (31K)

Fig. 1. HDPE material composition.

Display Full Size version of this image (58K)

Fig. 2. Joint geometry, cross section A-A.

The main defectives encountered in this particular product could be categorized into structural and adhesion. Structu

在研究之下的塑料联接通过挤出成型过程被做。 介入的材料是一个聚合物(高密度聚乙烯高密度聚乙烯)的二层综合与一个黏着性接口。 这构成在图1.碳颜料显示增加了到其中一变暗的高密度聚乙烯层能提供更好的热中子吸收和放射物产为绝缘材料目的。 联接的几何在检查之下的与一个横剖面一起在图2在二个杯子中显示，这几何代表一起被焊接在脖子区域。 政券接口位于在白色高密度聚乙烯层数和几何的其余之间。
这个图象(31K)的Display大型版本

Fig. 1.高密度聚乙烯材料构成。

这个图象(58K)的Display大型版本

Fig. 2.联合几何，横剖面A-A。

在这个特殊产品遇到的The主要defectives能被分类入结构和黏附力。 结构瑕疵在脖子区域包括不同心度和变异在联络直径，也许影响那些联接破损方式如图3.黏附力相关的瑕疵所显示包括缺乏黏附力、黏附力厚度、均一和分层法。 所有这些defectives终于影响联接力量。
这个图象(9K)的Display大型版本

Fig. 3.联络作用直径对联接的破损方式的。

In以下红外热熔印刷传输方式将被介绍并且申请技术可行性的检验通过学习政券正直的作用对热量波浪传导通过政券区域。 搏动的被反射的方式为厚度映射和分层法侦查也将被提出。