In order to study the recognition ability of TE-Ag NPs, a variety of transition and alkali metal ions (10 4 M) were added into the TE-Ag NP solution. As Fig. 3A shows, only Cd21 ions induce a distinct color change from yellow to red, which corresponds to a dramatic increase of the absorbance intensity at 550 nm (Fig. 3B). To quantify the spectral change at 394 nm and 550 nm, the absorbance ratio at two wavelengths

Fig. 2 UV-vis spectra of (a) PP–Ag NPs and (b) TE-Ag NPs recorded after 1 day. The inset shows the stability of (c) PP–Ag NPs and
(d)TE-Ag NPs.

Fig. 3 The photographic images (A), UV-vis spectra (B) and R
(A550/A394) (C) of TE-Ag NP solution in the presence of 0.1 mM different transition metal ions. Typically, 1 mL of 0.1 mM various transition metal ions were added into 1 mL TE-Ag NP solutions, and the combined solution mixed well for 30 min and then tested.

为了研究TE-Ag NPs的识别能力，在TE-Ag NP溶液中加入了多种过渡金属离子和碱金属离子（10 4M）。如图3A所示，只有Cd21离子感应从黄到红的显著的颜色变化，这与550nm波长处吸光度强度的巨大增加所相应（图3B）。为了量化394nm和550nm波长处的光谱变化，TE-Ag NPs在存在过渡金属离子时，在两个波长处的吸光率的比率（R＝A550/A394）进行了确定（图3C）。在存在Cd21时R值观察到了明显的提高。碱金属离子（图S6）和其他过渡金属离子对颜色或紫外吸收没有明显的影响，这表明了TE-NPs对Cd21是具有有效选择性的。作为一种对照，将过渡金属离子加入一种PP-Ag NPs的溶液中。被试验的大多数过渡金属离子可以使PP-Ag NPs的溶液在5分钟内改变颜色，这提示我们，在点击反应之前，Ag NPs对Cd21没有选择性的响应（图S7）。

图2 (a)PP-Ag NPs和(b) TE-Ag NPs在1天后记录的UV-vis光谱。插图显示(c) PP-Ag NPs和(d)TE-Ag NPs稳定性

图3 在存在0.1mM不同过渡金属离子时TE-Ag NPs溶液的照相图（A），UV-vis光谱和R(A550/A394)(C)。典型来说，将1mL的0.1mM不同过渡金属离子加入1mL的TE-Ag NPs溶液，而组合的溶液被很好混合30分钟，然后进行试验。

为了研究TE的识别能力银纳米粒，过渡和碱金属离子（10 4米）品种被纳入德银纳米粒子溶液补充。正如图。第3A表明，只有CD21的离子诱使从黄色变成红色，相当于一个在550 nm处的吸收强度显着增加（图3B）款不同颜色的变化。为了量化在394 nm和550 nm的光谱变化，在两个波长的吸收率

图。 2紫外可见（1）聚丙烯银核动力源（二）德银纳米粒谱记录后1天。该插图显示了（三）聚丙烯银纳米粒与稳定

（四）德银核动力源。

图。 3摄影作品（一），紫外可见光谱（乙）和R（A550/A394）（丙的TE）银纳米粒子溶液在0.1毫米不同过渡金属离子的存在。一般来说，1 0.1毫米的各种过渡金属离子毫升中加入1毫升德银纳米粒子

解决方案，合并后的解决方案，混合以及3