The particle size distribution of the Ch-zeolite was
determined using a laser diffraction equipment (CILASk
1064) and standard wet sieving (Mesh Tylerk
series).
Scanning electron microscopy (SEM-PHILIPSk
XL20) was used for photomicrographs as well as to
analyse the Ch-zeolite composition (Energy Dispersion
X-ray, EDX). The sample was initially placed in
a vacuum chamber for coating with a thin layer (few
nanometers) of gold (Au).
The specific surface area of the material was
measured by the methylene blue technique and by
nitrogen gas adsorption methods, with the latter also
providing information about particle porosity.
In the methylene blue adsorption method, aqueous
solutions (50 ml) of methylene blue (100 mg l 1) were
agitated using an orbital shaker (Marconik) for an
hour at room temperature in the presence of different
quantities of
2.2.1. 物理和物理化学的描述特性 Ch 泡沸石的颗粒大小发行是 确定使用laser 衍射设备(CILASk 1064) 和标准湿筛(滤网Tylerk 系列) 。 扫描电子显微镜术(SEM-PHILIPSk XL20) 被使用了为显微像片并且 分析Ch 泡沸石构成(能量分散作用 X-射线, EDX) 。样品最初地被安置了 真空分庭为给套上外套按薄层(少数 毫微米) 金子(Au) 。 材料的具体表面是 由次甲基蓝色技术测量和 氮气气体吸附方法, 与后者还 提供关于微粒多孔性的信息。 在次甲基蓝色吸附方法, 含水 解答(50 机器语言) 次甲基蓝色(100 毫克l 1) 是 鼓动使用一台轨道振动器(Marconik) 为 小时在室温在不同面前 Ch 泡沸石(0.05-0.3 g) 的数量。悬浮 然后被准许安定为23 h 和 收效的supernatants 被分离了在5000 转每分钟 在对残余的次甲基蓝色的分析之前 集中。结果被获得对应于平均 三个不同实验的价值。具体 表面由Langmuir 评估了 塑造, 承担形成, 以高浓度, 染料单层和1.08 nm2 分子1, 为 断面(范・den Hul 和Lyklema 1968) 。 Ch 泡沸石具体表面被评估了 由氮气气体吸附方法, 使用自动化 设备(Autosorb 1-Quantachrome Instrumentsk), 使用多点赌注等温线 吸附数据配件。并且从这数据, 材料的多孔性被评估了通过参量 譬如总毛孔(d < 的容量; 206 毫微米), micropores (d < 的表面和容量; 2 毫微米; Micropore 分析方法) 。 Zeta 潜在的测量为自然和 氨被装载的泡沸石, 作为媒介功能 酸碱度, 是坚定的使用Zeta Plusk 设备 (Brookhaven 仪器) 。悬浮(0.01% v/v) Ch 泡沸石, 早先筛在上午37 点以下 (400 捕捉Tylerk), 在一10 3 mol l 1 解答 KNO3 被使用了并且媒介酸碱度是受控的 增加硝酸(pH< 7) 和 KOH (pH>7), 分开地。为Ch 泡沸石饱和 与氨, 材料的悬浮是 由同样做法准备, 除了 样品用100 毫克NH3-N l 1 被装载了 氨。